ZINDN Coatings China Manufacturer Epoxy Zinc-rich Primer Paint ZD6030
Product Description
The utility model relates to a two-component high-solid and heavy anticorrosive epoxy zinc-rich primer composed of epoxy resin, zinc powder, solvent, auxiliary agent and polyamide curing agent.
The paint film has excellent anti-rust properties.
Can provide cathodic protection for local damaged areas;
It has excellent adhesion to the surface of carbon steel cleaned by jet.
Product Attributes
Color: Grey
Gloss: no light
Volume solid content: 58±3%
Mixing density (kg/L) : 1.75±0.1
Typical film thickness and theoretical coating rate:
|
Min |
Typical |
Max |
|
| Dry Film Thickness(μm) |
40 |
60 |
80 |
| Wet film thickness(μm) |
69 |
103.5 |
138 |
| Theoretical coating rate（kg/m2） |
0.121 |
0.181 |
0.241 |
Product Construction
Applicable Substrate And Surface Treatment:
New steel: Remove grease from the surface with an appropriate detergent and rinse the surface with fresh water for salt and other dirt. Remove the welding slag, smooth the weld and sharp edges, spray clean to Sa2.5 grade (ISO8501-1), the surface roughness reaches Rz40μm~75μm (medium roughness in the ISO8503-1 comparison plate) is the best, it is best to apply the primer within 4 hours after spray cleaning.Galvanized surface maintenance: use appropriate detergent to thoroughly remove the grease on the surface, wash off salt and other dirt with high-pressure fresh water, use power tools to polish small areas of rust, and recoat with this product.
Construction And Curing Environmental Conditions:
The construction environment temperature is 5~50 °C, the relative humidity of the air is not more than 80%, and the surface temperature of the steel should be greater than the dew point of 3 °C; Bad weather such as rain, fog, snow, strong wind and heavy dust is prohibited for outdoor use;In summer, the temperature is high, be careful with dry spraying, and during construction and drying in narrow spaces, a lot of ventilation is required;
Construction Method:
Airless spraying and air spraying are recommended, brush coating and roll coating are only recommended for pre-coating, small area painting or repair.
| Construction Method |
Units |
Airless spraying |
Air spraying |
Brush coating |
| Gun Aperture |
mm |
0.43～0.58 |
1.5～2.5 |
—— |
| Spray Pressure |
kg/cm2 |
150～200 |
3～4 |
—— |
| Dilute Release |
% |
0～10 |
10～20 |
5～10 |
High Drying/Curing Time And Coating Interval:
| Substrate Surface Temperature |
5℃ |
15℃ |
25℃ |
35℃ |
| Surface Dry |
5 Hour |
2 Hour |
0.5 Hour |
0.2 Hour |
| Harsh Drying Schedule |
24 Hour |
20 Hour |
14 Hour |
10 Hour |
| Self Coating Minimum Interval |
20 Hour |
15 Hour |
10 Hour |
6 Hour |
| Maximum Oating Interval |
Seven Days |
|||
Product Use
As a primer, it is used for the bare steel surface cleaned by jet in medium to severe corrosive environment, such as steel structure, bridge, port machinery, offshore platform, construction machinery, storage tank and pipeline, power facilities, etc., and the use of high-performance paint can further improve the corrosion resistance of the coating;Can be used on approved retained zinc-rich workshop primer surfaces;Can be used to repair damaged areas of galvanized parts or zinc silicate primer coating;Maintenance can only be used on the surface of the surface treated to bare steel to play its cathodic protection and rust prevention.