ZINDN Coatings China Manufacturer Anti-slip type Cold Galvanizing Compound ZD96-2
Product Description
One-component high-solids heavy-duty anticorrosive coating composed of fusion agent, zinc powder, anti-slip material, solvent, etc. The anti-slip coefficient meets the requirements of TB/T 1527-2011 and GB/T 50205-2020.
It can realize the spraying of zinc protective layer with a galvanizing content of more than 90% at room temperature;
It has excellent anti-rust performance;
It has excellent weather resistance;
Excellent adhesion;
Anti-slip coefficient≥ 0.55;
Easy to patch;
The construction is convenient and the drying is fast.
Product Attributes
Gloss: Matteless
Volumetric solids: 51±3%
Density (kg/L): 2.7±0.1
Typical Film Thickness and Theoretical Coating Rate:
|
Min |
Typical |
Max |
|
| Dry Film Thickness(μm) |
40 |
60 |
80 |
| Wet film thickness(μm) |
78.4 |
117.6 |
156.8 |
| Theoretical coating rate（kg/m2） |
0.211 |
0.316 |
0.422 |
Product Construction
Applicable Substrate And Surface Treatment:
New steel: Remove grease from the surface with an appropriate detergent and rinse the surface with fresh water for salt and other dirt. Remove the welding slag, smooth the weld and sharp edges, spray clean to Sa2.5 grade (ISO8501-1), the surface roughness reaches Rz40μm~75μm (medium roughness in the ISO8503-1 comparison plate) is the best, it is best to apply the primer within 4 hours after spray cleaning.Galvanized surface maintenance: use appropriate detergent to thoroughly remove the grease on the surface, wash off salt and other dirt with high-pressure fresh water, use power tools to polish small areas of rust, and recoat with this product.
Construction And Curing Environmental Conditions:
The construction environment temperature is 5~50 °C, the relative humidity of the air is not more than 80%, and the surface temperature of the steel should be greater than the dew point of 3 °C; Bad weather such as rain, fog, snow, strong wind and heavy dust is prohibited for outdoor use;In summer, the temperature is high, be careful with dry spraying, and during construction and drying in narrow spaces, a lot of ventilation is required;
Construction Method:
Airless spraying and air spraying are recommended, brush coating and roll coating are only recommended for pre-coating, small area painting or repair.
| Construction Method |
Units |
Airless spraying |
Air spraying |
Brush coating |
| Gun Aperture |
mm |
0.43～0.53 |
1.5～2.5 |
—— |
| Spray Pressure |
kg/cm2 |
150～200 |
3～4 |
—— |
| Dilute Release |
% |
0～5 |
5～10 |
0～5 |
High Drying/Curing Time And Coating Interval:
| Substrate surface temperature |
5℃ |
15℃ |
25℃ |
35℃ |
| surface dry |
1 Hour |
45 Minute |
15 Minute |
10 Minute |
| harsh drying schedule |
3 Hour |
2 Hour |
1 Hour |
45 Minute |
| Self coating minimum interval |
2 Hour |
1 Hour |
30 Minute |
30 Minute |
| Minimum interval between coats of sealer |
36 Hour |
24 Hour |
18 Hour |
12 Hour |
| Maximum oating interval |
Before applying the next coating, the surface should be clean and dry and free of zinc salts and contaminants |
|||
Product Use
It is used for the coating of the friction surface of high-strength bolt connection, which can replace thermal spray zinc and inorganic zinc-rich anti-skid coatings, and is widely used in railways, highway bridges, wind power, port machinery and other fields.