A two component, tetra fluorocarbon resin, aliphatic isocyanate cured topcoat, good weather, color retention and chemicals resistance, self-cleaning performance
Features
1.Highly decorative, super anti-ultraviolet performance, excellent weather resistance;
2.The paint film is bright and clean, not easy to be stained with dirt, and has good self-cleaning performance.
3.High solids and low VOC, no chlorine, fluorine content of solvent soluble matter is not less than 24%.
4.Excellent chemical resistance, good permeability resistance, outstanding corrosion resistance.
Recommended use
Excellent industrial protection and decorative finish, suitable for steel structures or concrete surfaces in various harsh atmospheric environments, such as large steel structures, bridges, offshore platforms, outer walls of storage tanks, ship superstructures, petrochemical equipment, and engineering machinery Equipment, etc. It is especially suitable for surfaces with extremely high requirements for gloss and color retention.
Application Instructions
Applicable Substrate and Surface Treatments:
Use a suitable cleaning agent to remove all grease and dirt on the substrate surface, and keep the surface clean, dry and pollution-free.
This product must be applied on the recommended anti-rust coating within the specified recoating interval.
The damaged parts of the primer must be blasted to Sa.2.5 (ISO8501-1) or power-treated to St3 standard, and prime paint should be applied to these parts.
Applicable and Curing
1.Substrate surface must be kept clean and dry, and the temperature of the substrate must be 3°C above the dew point to avoid condensation.
2.This product can also be reacted and cured at a temperature as low as -10°C, as long as there is no frost on the surface.
3.Outdoor application is prohibited in severe weather such as rain, fog, snow, strong wind and heavy dust.
4.The temperature is high in summer, be careful with dry spraying, and keep ventilated
5.during application and drying periods in narrow spaces.
Pot life
| 5℃ | 15℃ | 25℃ | 35℃ |
| 6 hrs. | 5 hrs. | 4 hrs. | 2.5hrs. |
Application
It is suitable for overcoating on the previous coatings such as epoxy or polyurethane, and used as a protective high-decorative weather-resistant topcoat for metal structures or concrete surfaces in various atmospheric environments.
Pot Life
| Application method | Unit | Airless spray | Air spray | Brush/Roller |
| Nozzle orifice | mm | 0.35～0.53 | 1.5～2.5 | —— |
| Nozzle pressure | kg/cm2 | 150～200 | 3～4 | —— |
| Thinner | % | 0～10 | 10～25 | 5～10 |
Drying & Curing
| Substratetemperature | -5℃ | 5℃ | 15℃ | 25℃ | 35℃ |
| Surface-dry | 2hrs. | 1hr | 45mins | 30mins | 20min |
| Through-dry | 48hrs. | 24 hrs. | 12 hrs. | 8 hrs. | 4h |
| Min. Recoating interval time | 36 hrs. | 24 hrs. | 12 hrs. | 8 hrs. | 4h |
| Max. Recoating interval time | 30 days | ||||
Preceding & Consequent coating
Preceding paint: all kinds of epoxy, polyurethane intermediate paint or anti-rust primer, please consult Zindn
Packing & Storage
Packing：base 25kg，curing agent 2.5kg
Flash point：>25℃（Mixture）
Storage ： Must be stored in accordance with local governmental regulations. The storage
environment should be dry, cool, well-ventilated and away from heat and fire sources. The
packaging container must be kept tightly closed.
Shelf life：1 year under good storage conditions from time of production.